Is the whole thing not curing, or just some parts?
Did you stir up the Part B before you started?
How old is the product? Has it been opened before?
Mold max 30 is a tin-cure silicone, so it's probably not cure inhibition from your model or sealer or release, but apparently that's still possible... Are you using a sulfur-based clay, or an odd release agent or anything?